Non-Asbestos Jointing Sheets KNXB200

Non-Asbestos Jointing Sheets KNXB200

Product number:KNXB200

Quick Overview: Non-Asbestos Jointing Sheets are made of special non-asbestos heat-resisting Fibre, heat-resisting packing material, and special rubber compound heating and compression molding it.

Send Inquiry

PDF DownLoad

Product Description

KNXB200 Non-Asbestos Jointing Sheets KNXB300 Non-Asbestos Jointing Sheets
KNXB350 Non-Asbestos Jointing Sheets KNNY150 Non-Asbestos Jointing Sheets
KNNY250 Non-Asbestos Jointing Sheets KNNY300 Non-Asbestos Jointing Sheets
KNNY350 Non-Asbestos Jointing Sheets

Non-Asbestos Jointing Sheets are made of special non-asbestos heat-resisting Fibre, heat-resisting packing material, and special rubber compound heating and compression molding it.

Material: Made of special non-asbestos heat-resisting Fibre, heat-resisting packing material and nature rubber compound heating and compression molding it.
Uses: Substitution of corresponding models of asbestos rubber sheet ,Used for the equipment in water,steam,etc.and used as sealing material in the joints of pipeline
Working pressure : 1.5 MPa ,Working temperature : 200
Sizes:
4100 x 1500 x (0.5 - 6.0)mm,  2000 x 1500 x  (0.5 - 6.0)mm,
1500 x 1360 x (0.5 - 6.0)mm,  3810 x 1270 x (0.5 - 6.0)mm
1270 x 1270 x (0.5 - 6.0)mm,  1500 x 1500 x (0.5 - 6.0)mm

The other size is optional or according to the requirements of customers.

Packing: in wooden pallet of about 1000 kgs, 2000kgs net each.

Item

KNXB200

KNXB300

KNXB350

KNNY150

KNNY250

KNNY300

KNNY350

Tensile strength MPa

5.0

7.0

11.0

8.0

10.0

12.0

15.0

Aging Coefficient

0.9

Density   g/cm³

1.6 - 2.0

1.6 - 1.8

Compressibility %

12 7

Rebound degree

35

40

45

40

45

50

50

Pliability

No Crack

Stress-relaxation

45

45

45

40

40

30

30

Oil sealing
With the temperature
of 15to 30,.75#aviation gasoline for 30 min




10 MPa pressure for 30 min
No leaking

12 MPa pressure for 30 min
No leaking

15MPa pressure for 30 min
No leaking

16 MPa pressure for 30 min
No leaking

With the temperature of 1502,dipped in No.20 aviation oil for 5h,then taken out and laid for 5min.

Tensile strength-reducing %

40

30

25

25

Thickness-increasing %

5-20

5-20

5-18

5-18

Appearance change

No bubble

With the temperature
of 15 to 30 ,dipped in No.75 aviation oil for 5h,then taken out and laid for 5min.

Tensile strength MPa

5

6

8

10

Thickness-increasing %

5-25

5-25

5-20

5-20

Pliability

No Crack